Polyaniline nanoparticle coated graphene oxide composite nanoflakes for bifunctional multicolor electrochromic and supercapacitor applications | |
Zhang, Sihang1; Chen, Sheng2; Cao, Ya1; Yang, Feng1; Peng, Hongchao2; Yan, Bin2; Jiang, Hao3; Gu, Yingchun2; Xiang, Ming1 | |
2019-07-01 | |
摘要 | Graphene oxide (GO)/polyaniline (PANI) composite nanoflakes were fabricated by chemical oxidative polymerization of aniline onto GO nanoflakes. The electrochromic properties and the electrochemical capacitive behaviors of the GO/PANI composite nanoflake film were investigated. The GO/PANI nanocomposite film exhibits excellent electrochromic and supercapacitive performances. In comparison with neat PANI film, the GO/PANI composite nanoflake film shows larger optical modulation, faster response speed, larger coloration efficiency and better cycling stability. Moreover, an areal capacitance of (137 mF/cm(2)) is obtained for GO/PANI nanoflake film at a scanning rate of 5 mV/s, higher than that of neat PANI film (36 mF/cm(2)). The GO/PANI composite nanoflake film also shows enhanced electrochromic and supercapacitive durability. And the electrochromism also could be utilized as an indicator for the capacitance. The high-performance GO/PANI nanocomposite film shows promising features for multifunctional devices combining energy storage and electrochromism. |
DOI | 10.1007/s10854-019-01717-y |
发表期刊 | JOURNAL OF MATERIALS SCIENCE-MATERIALS IN ELECTRONICS |
ISSN | 0957-4522 |
卷号 | 30期号:14页码:13497-13508 |
通讯作者 | Chen, Sheng(chensheng@scu.edu.cn) ; Gu, Yingchun(guyingchun@scu.edu.cn) |
收录类别 | SCI |
WOS记录号 | WOS:000476518000067 |
语种 | 英语 |