Mechanical properties and friction behaviors of CNT/AlSi10Mg composites produced by spark plasma sintering | |
Wang, Lin-zhi1,2; Liu, Ying2; Wu, Jiao-jiao1; Zhang, Xi3 | |
2017-05-01 | |
摘要 | The mechanical properties and friction behaviors of CNT/AlSi10Mg composites produced by spark plasma sintering (SPS) were investigated. The results showed that the densities of the sintered composites gradually increased with increasing sintering temperature and that the highest microhardness and compressive strength were achieved in the specimen sintered at 450A degrees C. CNTs dispersed uniformly in the Al-Si10Mg matrix when the addition of CNTs was less than 1.5wt%. However, when the addition of CNTs exceeded 1.5wt%, the aggregation of CNTs was clearly observed. Moreover, the mechanical properties (including the densities, compressive strength, and microhardness) of the composites changed with CNT content and reached a maximum value when the CNT content was 1.5wt%. Meanwhile, the minimum average friction coefficient and wear rate of the CNT/AlSi10Mg composites were obtained with 1.0wt% CNTs. |
关键词 | metal matrix composites carbon nanotubes (CNTs) aluminum silicon magnesium alloys spark plasma sintering mechanical properties friction |
DOI | 10.1007/s12613-017-1440-3 |
发表期刊 | INTERNATIONAL JOURNAL OF MINERALS METALLURGY AND MATERIALS |
ISSN | 1674-4799 |
卷号 | 24期号:5页码:584-593 |
通讯作者 | Liu, Y (reprint author), Sichuan Univ, Coll Mat Sci & Engn, Chengdu 610065, Peoples R China. |
收录类别 | SCI |
WOS记录号 | WOS:000400653700013 |
语种 | 英语 |