| Colloidal synthesis of Cu2-xAgxCdSnSe4 nanocrystals: microstructures facilitate high performance thermoelectricity | |
Chen, Qiufan1; Wang, Guiwen1; Zhang, Aijuan1; Yang, Dingfeng2; Yao, Wei1; Peng, Kunling1,2; Yan, Yanci1; Sun, Xiaonan1; Liu, Anping1; Wang, Guoyu2
| |
| 2015 | |
| 摘要 | In this study, we report the colloidal synthesis (CS) of quaternary chalcogenide Cu2-xAgxCdSnSe4 nanocrystals (x = 0, 0.1, 0.2, 0.3, and 0.4) and their application in thermoelectrics. The as-prepared Cu2-xAgxCdSnSe4 nanocrystals present a narrow size distribution ranging from 30 to 50 nm and a precisely controlled composition. Additionally, it was observed that the disordered zinc blende phases were embedded in the normal zinc blende phases and amorphous nanoparticles were dispersed on grain surfaces and between grain boundaries of spark plasma sintered bulk Cu2-xAgxCdSnSe4. Moreover, a large enhancement in the Seebeck coefficient and a dramatically reduced lattice thermal conductivity was found in Cu2-xAgxCdSnSe4 solid solution, resulting in the dimensionless thermoelectric figure of merit reaching a peak value of 0.8 at 688 K when x = 0.3. This represents a 44% and 83% improvement in comparison to the undoped sample and the sample made via the solid state method (SS), respectively. The results demonstrate an exciting scientific opportunity to raise the figure-of-merit of quaternary chalcogenide Cu2CdSnSe4 prepared by colloidal synthesis via optimized solid solution. |
| DOI | 10.1039/c5tc02948a |
| 发表期刊 | JOURNAL OF MATERIALS CHEMISTRY C
 |
| ISSN | 2050-7526 |
| 卷号 | 3期号:47页码:12273-12280 |
| 通讯作者 | Zhou, XY (reprint author), Chongqing Univ, Dept Appl Phys, Chongqing 400044, Peoples R China. |
| 收录类别 | SCI |
| WOS记录号 | WOS:000365533600014 |
| 语种 | 英语 |