Enhanced anti-tribocorrosion property of a-C film under high hydrostatic pressure by high power pulsed magnetron sputter (HiPIMS) | |
Liu, Yingrui1,2,3; Li, Shuyu1,4; Zhou, Xiaohui1,5; Guo, Peng1; Chen, Rende1; Wei, Jing1; Wang, Aiying1,4; Ke, Peiling1,4 | |
2024-01-01 | |
摘要 | In this study, the amorphous carbon (a-C) films were deposited using HiPIMS and DCMS at same average power. The composition, microstructure and the anti-tribocorrosion property at hydrostatic pressure environment were investigated in detail. The results showed the HiPIMS:a-C film exhibited a higher fraction of sp3 bonding (59 %) compared to DCMS. The increased sp3 fraction led to improved mechanical properties and significantly enhanced the film's capacity loading during sliding. Furthermore, due to the denser structure, the HiPIMS:a-C film demonstrated enhanced localized corrosion resistance at 30 MPa, which can be attributed to its lower defect density. These findings highlight the substantial advantage of HiPIMS in producing high-performance a-C films suitable for harsh deep-sea environments. |
关键词 | a -C films HiPIMS tribocorrosion localized corrosion hydrostatic pressure |
DOI | 10.1016/j.jmrt.2023.12.197 |
发表期刊 | JOURNAL OF MATERIALS RESEARCH AND TECHNOLOGY-JMR&T |
ISSN | 2238-7854 |
卷号 | 28页码:3052-3067 |
通讯作者 | Ke, Peiling(kepl@nimte.ac.cn) |
收录类别 | SCI |
WOS记录号 | WOS:001166022800001 |
语种 | en |