Understanding the role of Pt addition on structure and thermal stability of CrWN glass molding coating in nitrogen molding atmosphere | |
Zhang, Weilun1; Yang, Di1; Gong, Feng2; Chen, Yongjun1; Chen, Tian3; Xie, Zhiwen1; Yang, Sirui4 | |
2024-02-01 | |
摘要 | A novel Pt doping was designed to improve the thermal stability of CrWN coating in a nitrogen atmosphere. The deposited CrWN coating possessed a multilayer structure and a coherent growth mode, resulting in considerable mechanical strength and large size grain. An uneven atomic migration also occurred during the coating depo-sition resulting in a coarse cluster surface. The W atom enrichment layer was rapidly oxidized during the ni-trogen annealing and thus led to serious mechanical degradation. The doping of Pt atoms effectively blocks the coherent growth of the grains, which creates a significant mixing effect, leading to a smooth surface with uniform element distribution. Although local incoherent growth compromised the mechanical behavior of CrWN-Pt coating, but the prominent pinning effect of dispersed Pt oxides can reduce oxidative erosion rate and stabilize the oxide layer up to some extent during nitrogen annealing. |
关键词 | CrWN coating Pt doping Nitrogen annealing Growth structure Thermal stability Precision glass molding |
DOI | 10.1016/j.vacuum.2023.112815 |
发表期刊 | VACUUM |
ISSN | 0042-207X |
卷号 | 220页码:11 |
通讯作者 | Gong, Feng(gongfeng@szu.edu.cn) ; Chen, Yongjun(chenyongjun-net@163.com) ; Xie, Zhiwen(xzwustl@126.com) |
收录类别 | SCI |
WOS记录号 | WOS:001127442700001 |
语种 | 英语 |