Effect of annealing heat treatment on microstructure and corrosion behavior of Ti6Al4V alloy fabricated by multi-laser beam wire-feed additive manufacturing in vacuum environment | |
Ding, Xueping1,2; Ma, Honglin2; Zhang, Qi2; Yang, Jie2; Li, Daoyuan2; Fan, Shuqian2 | |
2022-09-05 | |
摘要 | Ti6Al4V alloy thin wall was successfully fabricated by multi-laser beam wire-feed additive manufacturing in vacuum environment. The effect of annealing heat treatment (AHT) on microstructure and corrosion behavior of specimens in 3.5 wt% NaCl and 1 mol/L H(2)SO4 electrolytes was investigated. Results showed that AHT led to the reduction of the non-equilibrium phase alpha' and texture weakening. AHT700 was beneficial to achieve crystal refinement while AHT850 had obvious coarsening phenomenon. In addition, AHT could improve the corrosion behavior of the specimens due to the reduction of alpha' phase and relief of residual stress. Compared with the specimen of AHT850, the specimen of AHT700 with finer crystal size and obvious texture weakening improved the corrosion resistance more obviously. (C)& nbsp;2022 Elsevier B.V. All rights reserved. |
关键词 | Additive manufacturing Annealing heat treatment Ti6Al4V alloy Microstructure Corrosion behavior Vacuum |
DOI | 10.1016/j.jallcom.2022.165363 |
发表期刊 | JOURNAL OF ALLOYS AND COMPOUNDS |
ISSN | 0925-8388 |
卷号 | 914页码:11 |
通讯作者 | Fan, Shuqian(fansq@cigit.ac.cn) |
收录类别 | SCI |
WOS记录号 | WOS:000802566500002 |
语种 | 英语 |